Technical Parameters:
|
Items |
Part A |
Part B |
|
|
Before curing |
Appearance |
white |
brown |
|
Viscosity(mPa.s) |
22000±5000 |
200±50 |
|
|
Density(g/cm3) |
1.70±0.05 |
1.22-1.25 |
|
|
Use ration by weight A:B |
6：1 |
||
|
Specification |
Viscosity after mixing (mPa.s) |
3500±500 adjustable |
|
|
Operation time(min,25℃) |
30 adjustable |
||
|
Turnover time(min,25℃) |
150 adjustable |
||
|
Curing time(h,25℃) |
24 |
||
|
After curing |
Light yellow |
||
|
Shear strength(N/mm) |
19.85 |
||
|
Max peel force(N) |
990.63 |
||
|
Max peel strength(N/mm) |
99.06 |
||
|
Average peel force(N) |
717.77 |
||
|
Average peel strength(N/mm) |
71.78 |
||
|
Min peel force(N) |
455.87 |
||
|
Min peel strength(N/mm) |
45.59 |
||
Â
Â
|
Class |
Grade |
Efficiency |
Resistance |
Tensile Strength |
Thickness |
Basic Weight |
Stiffness |
|
HEPA |
H14 |
≥99.995% |
≤420Pa |
1.0-1.25KN/m |
0.33±0.02mm |
74±4g/m2 |
mg≥1000 |
|
H13 |
≥99.97% |
≤330Pa |
0.9-1.20KN/m |
0.33±0.02mm |
74±4g/m2 |
mg≥1000 |
|
|
H12 |
≥99.8% |
≤260Pa |
0.9-1.20KN/m |
0.33±0.02mm |
74±4g/m2 |
mg≥1000 |
|
|
H11 |
≥98% |
≤180Pa |
0.9-1.20KN/m |
0.33±0.02mm |
74±4g/m2 |
mg≥1000 |
|
|
H10 |
≥94% |
≤120Pa |
0.9-1.20KN/m |
0.33±0.02mm |
74±4g/m2 |
mg≥1000 |
|
|
ASHRAE |
F9 |
≥95% |
≤80Pa |
0.9-1.15KN/m |
0.33±0.02mm |
70±4g/m2 |
mg≥900 |
|
F8 |
≥90% |
≤60Pa |
0.9-1.15KN/m |
0.33±0.02mm |
70±4g/m2 |
mg≥900 |
|
|
F7 |
≥80% |
≤40Pa |
0.9-1.15KN/m |
0.33±0.02mm |
70±4g/m2 |
mg≥900 |
|
|
F6 |
≥60% |
≤25Pa |
0.9-1.15KN/m |
0.33±0.02mm |
70±4g/m2 |
mg≥900 |
Â
Specifications:
|
Model |
3016A |
|
Main Components |
polyolefin |
|
Color |
white |
- The product is a polymerized heat with 100% solid content molten adhesive, used as a solid state at room temperature
- 100% solid content, green and environmental protection Good adhesive properties for the filter element origami Lower adhesive temperature Better processing performance.
- No partition plate suitable for purification or other works Air filter molding, bonding and reinforcement.
Â
Softening Point (GB/T-15332) 110±5℃ viscosity /180℃ (GB/T-2794) 3500±800cps curing time
Â
Instructions for using:
Hotmelt tank: 140-160℃;hose：130-150℃; gun：120-135℃
Â
Storage:
- Store them in a dry, cool place and avoid them Direct sunlight, with a storage period of two years
- Do not mix them with other adhesives
- Wear personal protective equipment when operating
- to prevent high equipment Warm scald Advanced first use
- to avoid long-term glue in high temperature Stay and aging failure Please sure the bonding substrate surface is not contaminated
- To achieve a good bonding effect Long time shutdown should be timely emptied and washed machine.
- The product color will depend on the raw material batch Slightly different, but will not affect the usability ability